Citation: Hui-yun Sun, Tiao Yin, Jing-bo Zhao, Zhi-yuan Zhang, Wan-tai Yang. SYNTHESIS AND CHARACTERIZATION OF BIODEGRADABLE POLYESTERAMIDES CONSTRUCTED MAINLY BY ALTERNATING DIESTERDIAMIDE UNITS FROM N,N'-BIS(2-HYDROXYETHYL)-ADIPAMIDE AND DIACIDS[J]. Chinese Journal of Polymer Science, ;2013, 31(3): 452-461. doi: 10.1007/s10118-013-1233-8 shu

SYNTHESIS AND CHARACTERIZATION OF BIODEGRADABLE POLYESTERAMIDES CONSTRUCTED MAINLY BY ALTERNATING DIESTERDIAMIDE UNITS FROM N,N'-BIS(2-HYDROXYETHYL)-ADIPAMIDE AND DIACIDS

  • Corresponding author: Jing-bo Zhao, 
  • Received Date: 14 May 2012
    Revised Date: 22 August 2012

    Fund Project: This work was financially supported by the National Natural Science Foundation of China (Nos. 50873013 and 21244006).

  • Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N'-bis(2-hydroxyethyl)-adipamide and adipic acid or sebacic acid. Chain extension of them was conducted with 2,2¢-(1,4-phenylene)-bis(2-oxazoline) and adipoyl biscaprolactamate as combined chain extenders. The chain extended polyesteramides (ExtPEAs) were characterized by IR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering, tensile test and enzymatic degradation. The results showed that the ExtPEA(4,m)s were mainly constituted with the diester adipamide alternating units. ExtPEA(4,4) and ExtPEA(4,8) had Tm of 83.8℃ and 85.8℃ and initial decomposition temperature above 310.0℃. They crystallized similarly as Nylon-66 did and were flexible thermoplastic materials with tensile strength up to 25.64 MPa and strain at break up to 737%.
  • 加载中
    1. [1]

  • 加载中

Metrics
  • PDF Downloads(0)
  • Abstract views(791)
  • HTML views(4)

通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索
Address:Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888
Powered By info@rhhz.net

/

DownLoad:  Full-Size Img  PowerPoint
Return