Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

Citation: Gongqing Tang, Zhi-Guo Jiang, Xiaofeng Li, Hao-Bin Zhang, Zhong-Zhen Yu. Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites[J]. Chinese Journal of Polymer Science, 2014, 32(8): 975-985. doi: 10.1007/s10118-014-1488-8 shu

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

1.
State Key Laboratory of Organic-Inorganic Composites, Department of Polymer Engineering, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
2.
1. State Key Laboratory of Organic-Inorganic Composites, Department of Polymer Engineering, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
3.
2. Beijing Key Laboratory on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing 100029, China
4.
基金项目:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51125010 and 51221002) and the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20100010110006).

摘要: Simultaneous functionalization and reduction of graphene oxide (GO) is realized by refluxing of GO suspension with polyetheramine (D2000) followed by thermal treatment at 120℃. Compared to GO, the D2000-treated GO (GO-D2000) becomes hydrophobic, thermally stable and highly conductive with an electrical conductivity of 11 S/m, which is almost 8 orders of magnitude higher than that of GO. Due to the high conductivity and improved dispersion of GO-D2000, its epoxy nanocomposites exhibit a sharp transition from electrically insulating to conducting with a low percolation threshold of 0.71 vol%. With 3.6 wt% GO-D2000, the glass transition temperature of the epoxy nanocomposite is 27 K higher than that of neat epoxy.

关键词:

English

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

1.
State Key Laboratory of Organic-Inorganic Composites, Department of Polymer Engineering, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
2.
1. State Key Laboratory of Organic-Inorganic Composites, Department of Polymer Engineering, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
3.
2. Beijing Key Laboratory on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing 100029, China
4.
Received Date: 13 February 2014
Revised Date: 13 May 2014
Available Online: 05 August 2014
Fund Project:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51125010 and 51221002) and the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20100010110006).

Abstract: Simultaneous functionalization and reduction of graphene oxide (GO) is realized by refluxing of GO suspension with polyetheramine (D2000) followed by thermal treatment at 120℃. Compared to GO, the D2000-treated GO (GO-D2000) becomes hydrophobic, thermally stable and highly conductive with an electrical conductivity of 11 S/m, which is almost 8 orders of magnitude higher than that of GO. Due to the high conductivity and improved dispersion of GO-D2000, its epoxy nanocomposites exhibit a sharp transition from electrically insulating to conducting with a low percolation threshold of 0.71 vol%. With 3.6 wt% GO-D2000, the glass transition temperature of the epoxy nanocomposite is 27 K higher than that of neat epoxy.

Key words:

1. [1]
  Novoselov, K.S., Geim, A.K., Morozov, S.V., Jiang, D., Zhang, Y., Dubonos, S.V., Grigorieva, I.V. and Firsov, A.A., Science, 2004, 306(5696): 666
2. [2]
  Zhu, Y., Murali, S., Cai, W., Li, X., Suk, J.W., Potts, J.R. and Ruoff, R.S., Adv. Mater., 2010, 22(35): 3906
3. [3]
  Rao, C.N.R., Sood, A.K., Subrahmanyam, K.S. and Govindaraj, A., Angew. Chem. Int. Ed., 2009, 48(42): 7752
4. [4]
  Geim, A.K. and Novoselov, K.S., Nat. Mater., 2007, 6(3): 183
5. [5]
  Stankovich, S., Dikin, D.A., Dommett, G.H.B., Kohlhaas, K.M., Zimney, E.J., Stach, E.A., Piner, R.D., Nguyen, S.T. and Ruoff, R.S., Nature, 2006, 442(7100): 282
6. [6]
  Singh, V., Joung, D., Zhai, L., Das, S., Khondaker, S.I. and Seal, S., Prog. Mater. Sci., 2011, 56(8): 1178
7. [7]
  Xu, Y.X., Hong, W.J., Bai, H., Li, C. and Shi, G.Q., Carbon, 2009, 47(15): 3538
8. [8]
  Huang, L., Li, C., Yuan, W.J. and Shi, G.Q., Nanoscale, 2013, 5(9): 3780
9. [9]
  Fang, M., Zhang, Z., Li, J., Zhang, H., Lu, H. and Yang, Y., J. Mater. Chem., 2010, 20(43): 9635
10. [10]
  Tan, Y.Q., Song, Y.H. and Zheng, Q., Chinese J. Polym. Sci., 2013, 31(3): 399
11. [11]
  Wang, Z., Tang, X.Z., Yu, Z.Z., Guo, P., Song, H.H. and Du. X.S., Chinese J. Polym. Sci., 2011, 29(3): 368
12. [12]
  Zhang, H.B., Yan, Q., Zheng, W.G., He, Z. and Yu, Z.Z., ACS Appl. Mater. Interfaces 2011, 3(3): 918
13. [13]
  Wang, B.J., Zhang, Y.J., Zhang, J.Q., Gou, Q.T., Wang, Z.B., Chen, P. and Gu, Q., Chinese J. Polym. Sci., 2013, 31(4): 670
14. [14]
  Wang, G.S., Wei, Z.Y., Sang, L., Chen, G.Y., Zhang, W.X., Dong, Z.F. and Qi, M., Chinese J. Polym. Sci., 2013, 31(8): 1148
15. [15]
  Wang, Y., Yang, R., Shi, Z., Zhang, L., Shi, D., Wang, E. and Zhang, G., ACS Nano, 2011, 5(5): 3645
16. [16]
  Khan, U., May, P., O'Neill, A. and Coleman, J.N., Carbon, 2010, 48(14): 4035
17. [17]
  Park, S. and Ruoff, R.S., Nat. Nanotechnol., 2009, 4(4): 217
18. [18]
  Amarnath, C.A., Hong, C.E., Kim, N.H., Ku, B.C., Kuila, T. and Lee, J.H., Carbon, 2011, 49(11): 3497
19. [19]
  Li, D., Muller, M.B., Gilje, S., Kaner, R.B. and Wallace, G.G., Nat. Nanotechnol., 2008, 3(2): 101
20. [20]
  Stankovich, S., Dikin, D.A., Piner, R.D., Kohlhaas, K.A., Kleinhammes, A., Jia, Y., Wu, Y., Nguyen, S.T. and Ruoff, R.S., Carbon, 2007, 45(7): 1558
21. [21]
  Lee, L.J., Zeng, C., Cao, X., Han, X., Shen, J. and Xu, G., Compos. Sci. Technol., 2005, 65(1516): 2344
22. [22]
  Si, Y. and Samulski, E.T., Nano Lett., 2008, 8(6): 1679
23. [23]
  Wang, G., Yang, J., Park, J., Gou, X., Wang, B., Liu, H. and Yao, J., J. Phys. Chem. C, 2008, 112(22): 8192
24. [24]
  Wang, Y., Shi, Z. and Yin, J., ACS Appl. Mater. Interfaces, 2011, 3(4): 1127
25. [25]
  Khanra, P., Kuila, T., Kim, N.H., Bae, S.H., Yu, D.S. and Lee, J.H., Chem. Eng. J., 2012, 183: 526
26. [26]
  Xu, L.Q., Yang, W.J., Neoh, K.G., Kang, E.T. and Fu, G.D., Macromolecules, 2010, 43(20): 8336
27. [27]
  Li, W., Tang, X.Z., Zhang, H.B., Jiang, Z.G., Yu, Z.Z., Du, X.S. and Mai, Y.W., Carbon, 2011, 49(14): 4724
28. [28]
  Ma, H.L., Zhang, H.B., Hu, Q.H., Li, W.J., Jiang, Z.G., Yu, Z.Z. and Dasari, A., ACS Appl. Mater. Interfaces, 2012, 4(4): 1948
29. [29]
  Lan, T. and Pinnavaia, T.J., Chem. Mater., 1994, 6(12): 2216
30. [30]
  Ma, J., Meng, Q., Zaman, I., Zhu, S., Michelmore, A., Kawashima, N., Wang, C.H. and Kuan, H.C., Compos. Sci. Technol., 2014, 91: 82
31. [31]
  Zeng, C.F., Tang, Z.H., Guo, B.C. and Zhang, L.Q., Phys. Chem. Chem. Phys., 2012, 14: 9838
32. [32]
  Schniepp, H.C., Li, J.L., McAllister, M.J., Sai, H., Adamson, D.H., Prud'homme, R.K., Car, R., Saville, D.A. and Aksay, I.A., J. Phys. Chem. B, 2006, 110(17): 8535
33. [33]
  Ma, H.L., Zhang, H.B., Hu, Q.H., Li, W.J., Jiang, Z.G., Yu, Z.Z. and Dasari, A., ACS Appl. Mater. Interfaces, 2012, 4(4): 1948
34. [34]
  Zhou, T.N., Chen, F., Liu, K., Deng, H., Zhang, Q., Feng, J.W. and Fu, Q.A., Nanotechnology, 2011, 22: 045704
35. [35]
  Zhang, D.D., Zu, S.Z. and Han, B.H., Carbon, 2009, 47: 2993
36. [36]
  Kudin, K.N., Ozbas, B., Schniepp, H.C., Prud'homme, R.K., Aksay, I.A. and Car, R., Nano Lett., 2007, 8(1): 36
37. [37]
  Rafiee, M.A., Rafiee, J., Srivastava, I., Wang, Z., Song, H., Yu, Z.Z. and Koratkar, N., Small, 2010, 6(2): 179
38. [38]
  Ramanathan, T., Abdala, A.A., Stankovich, S., Dikin, D.A., Herrera-Alonso, M., Piner, R.D., Adamson, D.H., Schniepp, H.C., Chen, X. and Ruoff, R.S., Nat. Nanotechnol., 2008, 3(6): 327
39. [39]
  Lu, H. and Nutt, S., Macromolecules, 2003, 36(11): 4010
40. [40]
  Koerner, H., Misra, D., Tan, A., Drummy, L., Mirau, P. and Vaia, R., Polymer, 2006, 47(10): 3426
41. [41]
  Zaman, I., Phan, T.T., Kuan, H.C., Meng, Q., Bao, L.T., Youssf, O. and Ma, J., Polymer, 2011, 52(7): 1603
42. [42]
  Bao, C., Guo, Y., Song, L., Kan, Y., Qian, X. and Hu, Y., J. Mater. Chem., 2011, 21(35): 13290
43. [43]
  Zhang, H.B., Zheng, W.G., Yan, Q., Yang, Y., Lu, Z.H., Wang, J.W., Ji, G.Y. and Yu, Z.Z., Polymer, 2010, 51(5): 1191

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 929
HTML全文浏览量: 18

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

English

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

English

Simultaneous Functionalization and Reduction of Graphene Oxide with Polyetheramine and Its Electrically Conductive Epoxy Nanocomposites

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs