Copolymerization of -Methylstyrene and Styrene

Citation: Qian Liu, Lian-ying Liu, Yu-hong Ma, Chang-wen Zhao, Wan-tai Yang. Copolymerization of -Methylstyrene and Styrene[J]. Chinese Journal of Polymer Science, 2014, 32(8): 986-995. doi: 10.1007/s10118-014-1469-y shu

Copolymerization of -Methylstyrene and Styrene

1.
1. College of Material Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
2.
2. State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
3.
4.
College of Material Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
基金项目:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51033001 and 21074006).

摘要: In this paper, the effects of temperature from 60℃ to 80℃ and the molar ratios in monomer feed on the copolymerization of a-methylstyrene (AMS) and styrene (St) were studied. The resulting copolymers, designated as PAS, were characterized by FTIR, GPC, NMR and TGA. When the reaction temperature was below 75℃, the molecular weights increased almost linearly as the evolution of the copolymerization. The phenomenon revealed that AMS could mediate the conventional free radical polymerization having some features of a controlled system. As the AMS/St=50/50 (molar) in feed, the overall fraction of the AMS unit incorporated into the copolymer was as high as 42 mol%, the monomer conversion could be more than 90 wt% and the molecular weights could reach as high as 4400. However, since the styrene is more reactive than AMS, the AMS fraction in copolymer increased with the overall monomer conversion. The 13C-NMR revealed the products were random copolymers which had triads, such as -AMS-AMS-AMS-, -St-AMS-AMS- (-AMS-AMS-St-) and -St-AMS-St-. TGA curves demonstrated that the degradation temperature of the resulting copolymers went down from about 356.9℃ (0 mol% AMS) to 250.2℃ (42 mol% AMS). This behavior demonstrated that there exist weak bonds in the AMS-containing sequences which could be used as potential free radical generators.

关键词:

English

Copolymerization of -Methylstyrene and Styrene

1.
1. College of Material Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
2.
2. State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
3.
4.
College of Material Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
Received Date: 07 November 2013
Revised Date: 22 December 2013
Available Online: 05 August 2014
Fund Project:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51033001 and 21074006).

Abstract: In this paper, the effects of temperature from 60℃ to 80℃ and the molar ratios in monomer feed on the copolymerization of a-methylstyrene (AMS) and styrene (St) were studied. The resulting copolymers, designated as PAS, were characterized by FTIR, GPC, NMR and TGA. When the reaction temperature was below 75℃, the molecular weights increased almost linearly as the evolution of the copolymerization. The phenomenon revealed that AMS could mediate the conventional free radical polymerization having some features of a controlled system. As the AMS/St=50/50 (molar) in feed, the overall fraction of the AMS unit incorporated into the copolymer was as high as 42 mol%, the monomer conversion could be more than 90 wt% and the molecular weights could reach as high as 4400. However, since the styrene is more reactive than AMS, the AMS fraction in copolymer increased with the overall monomer conversion. The 13C-NMR revealed the products were random copolymers which had triads, such as -AMS-AMS-AMS-, -St-AMS-AMS- (-AMS-AMS-St-) and -St-AMS-St-. TGA curves demonstrated that the degradation temperature of the resulting copolymers went down from about 356.9℃ (0 mol% AMS) to 250.2℃ (42 mol% AMS). This behavior demonstrated that there exist weak bonds in the AMS-containing sequences which could be used as potential free radical generators.

Key words:

1. [1]
  Kim, J.K., Lee, H.H., Son, H.W. and Han, C.D., Macromolecules, 1998, 31: 8566
2. [2]
  Roland, C.M. and Casalini, R., Macromolecules, 2007, 40: 3631
3. [3]
  Moon, H.S., Kim, M.H. and Park, O.O., J. Appl. Polym. Sci., 2009, 111: 237
4. [4]
  Sharma, K.R., Polymer, 2000, 41: 1305
5. [5]
  Hoover, L.C. and Derimiggio, J.E., 1990, U.S. Pat., 4.972.232
6. [6]
  Lowry, G.G., J. Polym. Sci., 1960, 42: 463
7. [7]
  Higashimura, T., Kamigaito, M., Kato, M., Hasebe, T. and Sawamoto, M., Macromolecules, 1993, 26: 2670
8. [8]
  Cunningham, R.E., J. Appl. Polym. Sci., 1978, 22: 2907
9. [9]
  Hirao, A., Haraguchi, N. and Sugiyama, K., Macromolecules, 1999, 32: 48
10. [10]
  Jagur-Grodzinski, J., J. Polym. Sci. Part A: Polym. Chem., 2002, 40: 2116
11. [11]
  Wittmer, P., Adv. Chem. Ser., 1971, 99: 140
12. [12]
  Martinet, F. and Guillot, J., J. Appl. Polym. Sci., 1997, 65: 2297
13. [13]
  Martinet, F. and Guillot, J., J. Appl. Polym. Sci., 1999, 72: 1611
14. [14]
  Palmer, D.E., McManus, N.T. and Penlidis, A., J. Polym. Sci. Part A: Polym. Chem., 2001, 39: 1753
15. [15]
  Palmer, D.E., McManus, N.T. and Penlidis, A., J. Polym. Sci. Part A: Polym. Chem., 2000, 38: 1981
16. [16]
  Martinet, F. and Guillot, J., J. Appl. Polym. Sci., 1999, 72: 1627
17. [17]
  Wieland, P.C., Nuyken, O. and Raether, B., Macromol. Rapid Commun., 2001, 22: 700
18. [18]
  Kos, T., Strissel, C., Yagci, Y., Nugay, T. and Nuyken, O., Eur. Polym. J., 2005, 41: 1265
19. [19]
  Luo, Y.D., Chou, I.C., Chiu, W.Y. and Lee, C.F., J. Polym. Sci. Part A: Polym. Chem., 2009, 47: 4435
20. [20]
  Chen, D., Shi, Y. and Fu, Z.F., J. Appl. Polym. Sci., 2009, 111: 1581
21. [21]
  Ma, Y.H., Zhang, B., Zhao, C.W., Liu, L.Y., Jiang, S., Liang, S.J. and Yang, W.T., Acta Chim. Sinica, 2013, 71: 151
22. [22]
  Jiang, S., Deng, J.P. and Yang, W.T., Polym. J., 2008, 40: 543
23. [23]
  Jiang, S., Deng, J.P., Yu, Q. and Yang, W.T., J. Appl. Polym. Sci., 2011, 120: 466
24. [24]
  Jiang, S., Sun, A.P., Deng, J.P., Yang, W.T. and Yu, Q., J. Macromol. Sci. Part A: Pure Appl. Chem., 2011, 48: 846
25. [25]
  Jiang, S., Fang, X.H., Yu, Q., Deng, J.P. and Yang, W.T., J. Appl. Polym. Sci., 2012, 124: 4121
26. [26]
  Deng, J.P., Liang, S.J., Zhang, C.R., and Yang, W.T., Macromol. Rapid Commun., 2007, 28: 2163
27. [27]
  Jiang, S., Deng, J.P. and Yang, W.T., Macromol. Rapid Commun., 2008, 29: 1521
28. [28]
  Cui, L.L., Feng, S.G., Liu Y.F., Wang T. and Zhang, Q.W., 2001, U. S. Pat., 20.120.101.218A1
29. [29]
  Rudin, A. and Samanta, M.C., J. Appl. Polym. Sci., 1979, 24: 1665
30. [30]
  Rudin, A., Samanta, M.C. and Van Der Hoff, B.M.E., J. Polym. Sci. Polym. Chem. Ed., 1979, 17: 493
31. [31]
  Rudin, A. and Chiang, S.S.M., J. Polym. Sci. Polym. Chem. Ed., 1974, 12: 2235
32. [32]
  Nogueira, R.F. and Tavares, M.I.B., J. Appl. Polym. Sci., 2001, 81: 261
33. [33]
  Shibasaki, Y., Yang, M. and Sun, L., Polym. Adv. Technol., 2002, 13: 260

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 954
HTML全文浏览量: 23

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Copolymerization of -Methylstyrene and Styrene

English

Copolymerization of -Methylstyrene and Styrene

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Copolymerization of -Methylstyrene and Styrene

English

Copolymerization of -Methylstyrene and Styrene

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs