Ruthenium-modified porous NiCo2O4 nanosheets boost overall water splitting in alkaline solution
-
* Corresponding author.
E-mail address: xipx@lzu.edu.cn (P. Xi).
Citation:
Rui Yang, Xuezhao Shi, Yanyan Wang, Jing Jin, Hanwen Liu, Jie Yin, Yong-Qing Zhao, Pinxian Xi. Ruthenium-modified porous NiCo2O4 nanosheets boost overall water splitting in alkaline solution[J]. Chinese Chemical Letters,
;2022, 33(11): 4930-4935.
doi:
10.1016/j.cclet.2021.12.058
In the last hundred years, human civilization has been developed to a striking distance due to the discovery and use of fossil energy. However, the overuse of fossil fuels has brought two issues: environmental pollution and energy crisis [1-4]. With the increasing demand for renewable and clean energy, developing new-generation energy storage and conversion devices as promising alternatives to traditional fossil fuels is crucial [5, 6]. Hydrogen is known to be the optimal energy carrier due to its high energy density and accessibility from water electrolysis. Electrocatalytic water splitting is the best technology for hydrogen production owing to the non-polluting reactants and not any by-products, and it occurs as the reaction: 2H2O → 2H2 + O2 [7, 8]. Hence, hydrogen production from water electrolysis shows high promise [9].
Water splitting consists of two half reactions: the cathodic hydrogen evolution reaction (HER) and anodic oxygen evolution reaction (OER) [10-12]. The theoretical thermodynamic voltage for water splitting is 1.23 V. However, an additional overpotential is required to compensate the polarization-dependent loss. Generally, differentiated from the simple two-electron HER, OER needs to overwhelm the Gibbs energy barrier of four-step elementary reaction to proceed with the reaction thermodynamically [13, 14]. So far, the application of water splitting in industry is mainly generated H2 rather than O2, thereby the sluggish four-step OER determines the efficiency of the overall water-splitting reaction. Therefore, in order to achieve the high efficiency of hydrogen production, it is paramount to develop competent catalysts, which can be used in the water splitting at an appropriate rate driven by a lower overpotential. Currently, noble metal oxides such as IrO2 and RuO2 have been employed as the benchmarking electrocatalysts for OER, but they suffer from the high price and poor stability, which severely impede their large-scale application [15]. Thus, tremendous efforts have been devoted to developing earth-abundant transition-metal-based electrocatalysts for OER, such as metal oxides [16], hydroxides [17, 18], phosphates [19], chalcogenides [20], nitrides [21] and other metal-free materials [22].
Recently, transition metal carbides (TMCs) have attracted more attention in many catalytic fields due to the unique physicochemical properties, such as high stability, high electrical conductivity and high mechanical strength [23]. However, there are a few applications of carbides in electrocatalytic OER. On the one hand, carbides typically synthesized by the high temperature solid-state method, which made it difficult to large scale synthesize and application. On the other hand, their economic effects on industrial applications are not satisfied and too much energy is still being consumed in electrocatalytic water splitting. Excitedly, as the rapid development of nanotechnology, the investigations of carbides nanomaterials made tremendous advances in the past few decades [24, 25]. By regulating structure and composition, TMCs nanomaterials are high performance electrocatalysts with extremely potent. Herein, we review the recent research of TMCs to achieve high activity and long-term stability OER electrocatalysts. The objective of this paper is to discuss the current challenges and provide a possible strategy for the future development of OER catalyst synthesis.
Recently, carbide-based electrocatalysts with various morphologies, composition, and other additives have been aroused great interest owing to the satisfying disadvantages, such as the boosted reaction kinetics and stability. Numerous synthesis strategies have been explored to optimize nanostructures and compositions of carbide-based electrocatalysts (Table 1). In this section, we mainly focus on summarizing some typical synthetic methodology to obtain the high-efficiency carbide-based OER electrocatalysts.
By tuning the morphology of nanomaterials, a great deal of shapes such as nanospheres, nanorod, nanowire, nanosheet and so on, which could large activity surface area between catalysts and reactive species and more reaction sites for OER [26, 27]. That is one of the most important factors for determining the performance of a catalyst.
To enlarge the active surface area, a series of morphologies have been well designed. For example, Abe et al. prepared Ni3C nanoparticles (NPs) with a size smaller than 10 nm. Due to the large surface areas, the Ni3C NPs exhibit excellent catalytic activity toward to the electrooxidation of NaBH4 (Figs. 1a and b) [28]. Gao and colleagues have reported that successful synthesis of an effective cobalt-doping Mo2C nanowires (NWs) (Fig. 1c) [29]. The large surface in radial direction provides a large number of active sites, and the axial dimension advantageous to charge transfer and avoids material aggregation. As a result, the Co-doped Mo2C NWs showed high activity and excellent stability for electrocatalytic HER at both basic and acidic electrolytes. 2D nanomaterials represent a class of materials that show sheet-like structures, which possess the ultrathin thickness less than 5 nm with the width larger than 100 nm [26]. Except for NPs and NWs, nanosheets (NSs) such as 2D transition metal carbides (MXene) have shown greet competitive in energy storage [30-32]. For example, Barsoum et al. have reported that the large-scale synthesis of Mo2CTx flakes by etching of Ga from Mo2GaC (Fig. 1d) [33]. Due to the layered structure, large surface area, high conductivity, and mechanical properties, a large reversible capacity with 560 mAh/g has achieved under 0.4 A/g when the prepared materials were tested. Meanwhile, the Mo2CTx also showed excellent stability over 1000 cycles test. Vojvodic has also reported that the Mo2CTx as HER catalysts showed better activity and high stability in the acid electrolyte (Figs. 1e and f) [34].
For the individual catalyst often possess an excellent performance, some with abundant active sites, some showed high conductivity. Heterojunctions could combine the individual property of individual catalysts which have been demonstrated to be efficient catalysis for chemical reactions.
Non-noble metal carbide is an economical and widely applicable electrocatalyst. However, the intrinsic activity of pure-phase carbides is usually poverty for electrocatalysis. Therefore, in order to enhance the intrinsic activity of non-noble metal carbide, fabrication of heterojunctions catalyst is an effective method. For example, the g-C3N4 is a fascinating polymer semiconductor material for photocatalysis with a lot of advantages such as high chemical and thermal stability, excellent absorption properties, suitable band gap, easy fabrication, and low cost [35]. However, the sluggish reaction kinetics and fast recombination of the electron-hole pairs of g-C3N4 lead to a low quantum efficiency. Therefore, it is necessary to suppress recombination of electron-hole pairs of g-C3N4. By constructing nano-heterojunction, which could enhance the separation of electron-hole pairs and improve the surface reaction kinetics thus enhanced the photocatalytic performance. Li et al. have used Ni3C as cocatalysts to improve the performance of photocatalytic H2 evolution over the g-C3N4 (Fig. 2a) [36]. Compare to the quantum yield of pure g-C3N4, that of Ni3C NPs on g-C3N4 achieved an incredible promotion. The result also showed that the Ni3C/g-C3N4 possess excellent catalytic activity of photocatalytic H2 evolution (Fig. 2b). In the photocatalytic N2 reduction, the efficiency is too low due to the high bond energy of N≡N bond. Although various semiconductors have been investigated to N2 reduction, unfortunately, the photoelectron was not provided enough energy to make the cleavage of N≡N bond. Lam and co-workers have designed an in situ grown AnInS2 NPs@Ti3C2 NSs heterojunction (Fig. 2c), which can increase the energy of photoelectrons and promoting electronic accumulation on the surface of Ti3C2 [37]. The hybrids nanomaterial showed excellent photocatalytic N2 reduction ability due to the optimized structure (Fig. 2d). All in all, the heterojunction effect on catalytic applications has important potential values [38].
Despite there are low-cost and efficient of TMCs heterojunction, it is relatively seldom applied as the catalyst for electrocatalytic water splitting.
The surface electronic structure of catalysts is very important for the performance of the catalyst, which can control the adsorption of reactants and enhance the catalytic activity. The formation of multi-metallic structure is a common strategy to tune the property of electrocatalysts due to the interactions between different components, which is beneficial to tune the electronic structure and other physical and chemical properties of electrocatalysts then optimization the activities. This has been demonstrated by bimetallic [16, 39-42] and trimetallic [27, 43, 44] for efficient electrocatalysis.
For example, Zhang's group prepared bimetallic carbide Fe2MoC NPs, which can adjust the electronic properties of iron carbide. As a result, the Fe2MoC has been verified to possess excellent performance (Figs. 3a and b) [45]. In addition, more bimetallic carbides have been reported for high activity used in electrocatalysts field [46, 47]. Therefore, component control is an effective strategy to design high efficiency electrocatalyst.
In addition, doping is another effective way to boost the activity of catalysts. As a well know, by doping heteroatom into catalysts, the surface of catalysts is easier to turn to the oxidation state, then the energy barrier of OER could be effectively reduced and to boost catalytic performance [48-50]. Leonard has reported that the Fe-doped MoC NPs showed excellent HER catalytic performance [51]. The mechanism study demonstrates that Fe doping benefits to make lattice expansion and more electrons on catalyst surface around to Fermi level, which is the key factor to enhance the HER performance (Figs. 3c and d). Yan et al. has prepared Fe-doped Ni3C nanodots (NDs) based NSs [52]. By the introducing of Fe into the Ni3C NDs system, the as prepared material showed the best OER catalytic performance and the overpotential low to 275 mV at the current density of 10 mA/cm2. The results indicating that doping is an effective strategy to boost the performance of OER electrocatalysis.
Up to date, multi-component TMCs have recently been successfully applied in the studies of electrocatalytic OER process. However, more research is still needed to improve the stability of these TMCs electrocatalysts.
The stability of OER catalyst is also an important factor to determine the practical application. Therefore, substantial efforts also have been devoted to improving the stability of OER catalysis by tuning the structures. Among all the methods, the coating has been proven due to its superiority over the others in terms of enhancing stability, it is like that put catalyst in unique channel by graphene or other shell material. In this way, the metal catalyst can be protected and from damage in harsh conditions due to the shell can isolate the reaction molecules and catalyst.
Therefore, many different shell materials such as carbon nanotube, graphene and graphitic carbon nitride have been developed for the encapsulation. For example, the Fe3C NPs can be encapsulated in graphitic and dispersed on the N-doped graphene-like carbon sheets, the graphite layers around on the Fe3C NPs plays an important role in the significant stability of Fe3C@NG, which showed efficient electrocatalytic performance with high stability for ORR and OER (Figs. 4a-c) [53]. Carbon nanotube is an excellent material with high conductivity and high surface area. So, it can not only improve the stability, but also enhance the catalytic activity via encapsulating transition metal NPs into carbon nanotubes [54]. The transition metal NPs can be protected carbon layers, thus the catalysts possess superior stability (Figs. 4d and e). Significantly, due to the synergistic effects between core and carbon shell, the activity of the catalyst can also be enhanced. Wu et al. have reported carbon doped of N, O, S sheets-encapsulated Co9S8 nanomaterials and that material showed high activity and good stability in alkaline medium for OER. The excellent property is mainly due to the synergistic effects between the Co9S8 NPs and the multi-doped carbon in the materials [55].
Except for carbon materials, more 2D materials such as boron nitride, TM dichalcogenides and hydrotalcite can also be used for the encapsulation, which needs more studies to develop more excellent catalysts.
As discussed above, carbides nanomaterials have great potential for electrocatalytic water oxidation. TMC has very excellent physical and chemical properties such as high electrical conductivity, good corrosion resistance, and high mechanical stability. Despite there are still difficult in large-scale synthesis and application, many achievements have been obtained of carbide nanomaterials. In this section, several typical carbides including iron, cobalt and nickel carbide electrocatalysts will be introduced for electrocatalytic OER in recent years.
Compared to noble metal materials, non-noble transition metals have many advantages such as low price, abundant resources, and low toxicity. In the recent study, it is found that the transition metal carbides have "platinum-like" electronic excellent catalytic performance. Iron is the most abundant metallic element on earth, so that the iron carbide has great application prospect for electrocatalytic OER.
However, iron carbide catalysts often suffer from poor electrical conductivity and poor stability, which reduced their catalytic performance. Therefore, the best way to address the above issues is to design composite material of iron carbide and conductive carrier. An efficient catalyst employed in the reaction should satisfy the demand of binding energies between reactive intermediates and catalytic surface [56]. Synergetic carbides/graphene-like carbon multicomponent materials have many active sites and high surface areas, which benefit to the transport of electrolyte ions and adsorption of reactants [57, 58]. Encapsulated Fe3C NPs into porous carbon nitride [59], graphite [60], nitrogen functionalized carbon nanofibers [61] and N-doped carbon nanotubes [62], in which abundant porous can increase surface area and accelerating charge transfer thus to boost OER activity. For example, Lu and co-workers have designed Fe3C NSs@Ni foam (NF) nanocomposite by a one-step solvothermal and annealing method (Figs. 5a and b) [63]. The nanosheet structure of Fe3C can expose more active sites. Meanwhile, the unique three-dimensional structure of Fe3C@NF made it have good electrical conductivity, large surface area, and more active sites. As a result, the Fe3C@NF nanocomposite showed remarkable OER activity (Fig. 5c) amazing stability. Hierarchical structured of Fe/Fe3C NPs encapsulated by N-doped graphene also has been designed (Figs. 5d and e) [64]. The nanostructure showed high OER activity comparable to the RuO2 catalysts (Fig. 5f).
To date, although have made remarkable achievements, the exploration of new iron carbide with higher OER activity remains a long way for the industrial application.
Cobalt carbides (Co2C and Co3C) have been used in Fischer-Tropsch (FT) synthesis reaction [65]. Although a few studies have discussed for OER, cobalt carbides still have suffered high overpotential due to the low intrinsic activity and poor stability in a harsh electrolyte [66].
Bimetallic materials considered to be very important candidates because of introduction of a second metal into single metal materials can adjust the electronic structure of active center and expose more active sites [45, 46, 67] Therefore, bimetallic carbide materials are also considered as a potential catalyst for OER [68, 69]. Lan et al. have synthesized Co/Mo bimetallic carbide, which exhibits low overpotential of 260 mV, low Tafel slope and excellent stability (Figs. 6a and b) [47].
In addition, as an effective method to adjust the electronic structure of catalysts, heteroatom doping has been widely used in the synthesis of various catalysts. For example, Zhao et al. has reported a simple strategy of doping lower electronegative vanadium (V) into cobalt carbide, which results in most defects in the cobalt carbide lattice (Figs. 6c-e) [70]. Particularly, with the optimal doping amount, V0.28Co0.72C/carbon nanofibers (CNFs) display the best performance of electrocatalytic water splitting with the decomposition of 1.47 V at a current density of 10 mA/cm2. The main reason for the significant increase of overall water splitting is that the electron density transfer from V to cobalt makes the cobalt as a local negative center. Chen et al. have reported a N, B-codoping Co3C catalyst, which showed high OER activity with the overpotential of 358 mV, as well as improved stabilities [71]. In addition, the porous structure is beneficial for the catalyst to obtain higher OER activity due to the high surface area and expose more active sites. For example, He's group prepared a hierarchical porous Co3C/Co-N-C/G nanomaterial by a two-step method [72]. Due to more exposed active sites and the synergistic effects among all components, the as-prepared catalyst has shown high OER performance.
Nickel carbides are a promising electrocatalyst for OER due to the advantages of earth-abundance and superior electrical conductivity. Ni3C has attracted significant attention among various nickel carbide due to the excellent physicochemical properties such as high chemical stability and conductivity. For example, Xie et al. have synthesized Ni3C/C composite as OER catalyst, which displayed excellent bifunction catalytic activity of HER and OER [73].
Optimization of electrocatalytic performance is very important for developing nickel carbides OER catalysts. Zheng's group reported the Ni/Ni3C core/shell hierarchical nanospheres. Benefit by this structure, more active site has exposed, which exhibited an outstanding electrocatalytic performance with a low of 350 mV at 10 mA/cm2 for OER [74]. In order to improve the activity and stability of Ni/Ni3C catalyst, Zheng et al. have reported Ni3C/N-doped carbon nanoflakes, in which the structure and composition can be controlled by charge the synthetic conditions [75]. Based on the composite nanostructure, Ni3C/NC nanoflakes showed high electrocatalytic performance with a low overpotential of 309 mV. Yang et al. have fabricated N-doped carbon nanotubes encapsulated Ni/Ni3C-NCNT material, in which Ni3C NPs was uniformly distributed in the wall of NCNT (Figs. 7a and b) [76]. Due to the unique composition and structure, the sample displayed improved OER catalytic activity with a low overpotential of 277 mV (Fig. 7c).
In electrocatalysis process, active center of catalyst with different valence states possesses different adsorption and desorption energies to intermediates. Therefore, rationally adjust the valence is an effective method to boost the performance of the catalyst. Introduction of metals with different electronegativity can effectively regulate the valence state of catalyst. For example, the Zinc (Zn) can change the electronic property of bimetallic Ni3ZnC0.7 thus improved the OER activity (Figs. 7d-f) [77, 78]. Yang et al. have reported that a high-valence metals "Molybdenum" (Mo) is introduced into nickel carbide to form bimetallic Mo6Ni6C catalyst. In the catalytic process, high-valence Mo6+ has incorporated with the Ni species and the carbon element insert into MoNi array at the atomic level, which effectively enhances the conductivity and exposes more active sites. So, the bimetallic Mo6Ni6C showed amazing OER activity with an overpotential of 190 mV at a current density of 10 mA/cm2 [79].
Heteroatom doping adjusts the electron structure of catalysts can also promote electron transfer thus enhance the catalytic property. For instance, Li et al. have synthesized the Co-doped Ni3C/C compound material, which also showed outstanding OER catalytic performance compared to pure Ni3C [80]. In addition, high-index facets of catalyst usually have superior catalytic performance for OER. For this reason, Ma has prepared a high-index faceted NiC0.2 NSs on Ni-coated copper foil [81]. The as-prepared catalyst also showed high catalytic activity and long-term stability for OER (overpotential of 228 mV at 10 mA/cm2).
Among all carbides, the molybdenum/tungsten (Mo/W) carbides used to be HER catalysts in the past studies. However, the metals of carbides are converted to OER-active species during the OER process [82]. Hence, there is still plenty of room for improvement to become high activity OER catalyst. For instance, the B, N-codoped Mo2C NPs encapsulated on B, N-codoped carbon network present excellent performances of HER and OER (Figs. 8a and b) [83]. Jeon's group proposed a MoS2/Mo2C hybrid structure, in which the core-shell nanostructure showed excellent performance of ORR and OER with overpotential of 280 mV at 10 mA/cm2, better than that of most other molybdenum carbide catalyst. The lattice strain in the core/shell structure is responsible for high ORR and OER activity [84]. Similarly, tungsten carbides have been widely used as HER catalyst due to the similar d-electronic structure like platinum. However, the PbO2-WC composite has shown lower OER overpotential, indicating that WC has potential to be an efficient OER catalyst [85].
MXenes are promising materials for various energy storage devices and water splitting due to outstanding physicochemical properties such as high electrical conductivity, porosity, and stability. For example, Hao et al. have proposed an electrochemical etching method to synthesis MXenes (Fig. 8c) [86]. When the as-prepared material was employed to water oxidation (Fig. 8d), the catalytic performance is comparable to commercial IrO2. Due to the limitation of traditional synthesis method, the prepared 2D MXenes are dense and tend to stack together, which leads to a poor mass transfer and active sites for electrocatalytic water splitting. One approach to solve this problem is to assemble 2D MXenes into 3D structure. Wang et al. develop a pyrolysis method and surface engineering to prepare molybdenum carbide (Mo2CTx) 3D microflowers (MFs) structure (Fig. 8e) [87]. Benefit from the outstanding structural (Figs. 8f and g), such Mo2CTx showed ultrahigh electrocatalytic OER activity with an overpotential of only 180 mV to achieve a current density of 10 mA/cm2 (Fig. 8h). In addition, MXenes are potential carrier materials due to high surface area and electronegative surfaces, which may charge the electronic structure of the multicomponent catalyst thus most catalytic performance. For example, the MXenes can carry CoBDC MOF [88] or FeNi-LDH [89]. As a result, both MOF/Ti3C2Tx and FeNi-LDH/Ti3C2-MXene can exhibit superior activity and durability for OER. Manganese (Mn) carbide catalysts has also investigated for OER. For example, Streb's group synthesized metal oxides/carbides-CNT hybrid material with Mn/V oxide as a precursor [90].
In this review, we have summarized the development of transition metal carbides OER electrocatalysts, such as Fe-, Co-, Ni-, Mo-, W-based carbides, many strategies have been deployed to improve electrocatalytic performance for electrocatalytic OER, including morphology control, heterojunction, component control, and coating of conductive substrates. Although the transition metal carbides show high electron conductivity, desirable catalytic activity, and decent stability after the optimization of structure and composition, the performance of metal carbide is still not up to the level of the best catalyst such as layered double hydroxide. So, some problems should be solved as follows:
(1) The current synthesis methods for metal carbides possess obvious disadvantages which limit their large-scale application. With the development of materials science, it must develop a simple, efficient and widely used synthesis method to prepare transition metal carbide nanostructures.
(2) In the past design, metal carbide particles are usually spherical particles. For the morphologies design, this is very single. By designing carbide with special shape like cube, octahedral and polyhedron, we will further reveal the effect of crystal surface of metal carbide for electrocatalytic OER performance. So that to guide us to synthesize more efficient TMCs catalyst.
(3) It is remarkable that high-index facets of catalyst usually have superior catalytic performance for OER. Although various structures and morphologies have been designed, the design of high index carbide materials is rare. If we can design more carbide with a high index surface, it is hopeful to further improve the catalytic performance of carbide materials for OER.
As a great potential catalyst, metal carbides will have more applications in the future.
The authors declare no conflict of interest.
This work was supported by the National Natural Science Foundation of China (Nos. 51302079, 51702138), the Natural Science Foundation of Hunan Province (No. 2017JJ1008), and the Key Research and Development Program of Hunan Province of China (No. 2018GK2031).
Z.W. Seh, J. Kibsgaard, C.F. Dickens, et al., Science 355 (2017) eaad4998.
doi: 10.1126/science.aad4998
I. Roger, M.A. Shipman, M.D. Symes, et al., Nat. Rev. Chem. 1 (2017) 0003.
doi: 10.1038/s41570-016-0003
H. Sun, L. Chen, Y. Lian, et al., Adv. Mater. 32 (2020) 2006784.
doi: 10.1002/adma.202006784
J. Cao, C. Lei, J. Yang, et al., J. Mater. Chem. A 6 (2018) 18877.
doi: 10.1039/C8TA08337A
K. Wang, Wang X, Li Z, et al., Nano Energy 77 (2020) 105162.
doi: 10.1016/j.nanoen.2020.105162
L. An, J. Feng, Y. Zhang, et al., Adv. Funct. Mater. 29 (2019) 1805298.
doi: 10.1002/adfm.201805298
L. Wang, Z. Li, K. Wang, et al., Nano Energy 74 (2020) 104850.
doi: 10.1016/j.nanoen.2020.104850
C. Lei, S. Lyu, J. Si, et al., ChemCatChem 11 (2019) 5855–5874.
doi: 10.1002/cctc.201901707
F. Cheng, L. Wang, H. Wang, et al., Nano Energy 71 (2020) 104621.
doi: 10.1016/j.nanoen.2020.104621
C. Liu, J. Qian, Y. Ye, et al., Nat. Catal. 4 (2021) 36–45.
doi: 10.1038/s41929-020-00550-5
S.L. Zhang, B.Y. Guan, X.F. Lu, et al., Adv. Mater. 32 (2020) 2002235.
doi: 10.1002/adma.202002235
T. Wu, S. Sheng, J. Song, et al., Nat Catal. 2 (2019) 763–772.
doi: 10.1038/s41929-019-0325-4
J. Kim, H. Jung, S.M. Jung, et al., J. Am. Chem. Soc. 143 (2021) 1399–1408.
doi: 10.1021/jacs.0c10661
Q. Zhao, Z. Yan, C. Chen, et al., Chem. Rev. 117 (2017) 10121–10211.
doi: 10.1021/acs.chemrev.7b00051
J. Li, D. Chu, H. Dong, et al., J. Am. Chem. Soc. 142 (2020) 50–54.
doi: 10.1021/jacs.9b10882
J. Bao, X. Zhang, B. Fan, et al., Angew. Chem. Int. Ed. 54 (2015) 7399–7404.
doi: 10.1002/anie.201502226
Y. Sun, H. Liao, J. Wang, et al., Nat Catal. 3 (2020) 554–563.
doi: 10.1038/s41929-020-0465-6
Y. Duan, J.Y. Lee, S. Xi, et al., Angew. Chem., Int. Ed. 60 (2021) 7418–7425.
doi: 10.1002/anie.202015060
Y. Wen, P. Chen, L. Wang, et al., J. Am. Chem. Soc. 143 (2021) 6482–6490.
doi: 10.1021/jacs.1c00384
J. Yin, J. Jin, M. Lu, et al., J. Am. Chem. Soc. 142 (2020) 18378–18386.
doi: 10.1021/jacs.0c05050
R. Yang, L. An, Y. Zhang, et al., ChemCatChem 11 (2019) 6002–6007.
doi: 10.1002/cctc.201901634
J. Yang, B. Chen, X. Liu, et al., Angew. Chem. Int. Ed. 57 (2018) 9495–9500.
doi: 10.1002/anie.201804854
X. Wang, Y. Zheng, W. Sheng, et al., Mater. Today 36 (2020) 125–138.
doi: 10.1016/j.mattod.2019.12.003
X. Liu, F. Liu, J. Yu, et al., Adv. Sci. 7 (2020) 2001526.
doi: 10.1002/advs.202001526
S.Y. Bae, J. Mahmood, I.Y. Jeon, et al., Nanoscale Horiz. 5 (2020) 43–56.
doi: 10.1039/C9NH00485H
J. Su, Y. Yang, G. Xia, et al., Nat. Commun. 8 (2017) 14969.
doi: 10.1038/ncomms14969
C. Dong, X. Zhang, J. Xu, et al., Small 16 (2020) 1905328.
doi: 10.1002/smll.201905328
C. Wang, L. Qin, Angew. Chem. Int. Ed. 59 (2020) 17219–17224.
doi: 10.1002/anie.202005436
S. Jiang, R. Zhang, H. Liu, et al., J. Am. Chem. Soc. 142 (2020) 6461–6466.
doi: 10.1021/jacs.9b13915
Q. Lu, Y. Yu, Q. Ma, et al., Adv. Mater. 28 (2016) 1917–1933.
doi: 10.1002/adma.201503270
S.H. Ye, Z.X. Shi, J.X. Feng, et al., Angew. Chem. Int. Ed. 57 (2018) 2672–2676.
doi: 10.1002/anie.201712549
J. Yin, J. Jin, H. Zhang, et al., Angew. Chem. Int. Ed. 58 (2019) 18676–18682.
doi: 10.1002/anie.201911470
Y. Gu, A. Wu, Y. Jiao, et al., Angew. Chem. Int. Ed. 60 (2021) 6673–6681.
doi: 10.1002/anie.202016102
J. Yin, J. Jin, H. Liu, et al., Adv. Mater. 32 (2020) 2001651.
doi: 10.1002/adma.202001651
T.X. Nguyen, Y.C. Liao, C.C. Lin, et al., Adv. Funct. Mater. 31 (2021) 2101632.
doi: 10.1002/adfm.202101632
T. Zhao, X. Shen, Y. Wang, et al., Adv. Funct. Mater. 31 (2021) 2100614.
doi: 10.1002/adfm.202100614
J. Gao, C.Q. Xu, S.F. Hung, et al., J. Am. Chem. Soc. 141 (2019) 3014–3023.
doi: 10.1021/jacs.8b11456
D.J. Morgan, Surface Interf. Anal. 47 (2015) 1072–1079.
doi: 10.1002/sia.5852
J. Yang, C. Wang, H. Ju, et al., Adv. Funct. Mater. 27 (2017) 1703864.
doi: 10.1002/adfm.201703864
Y. Duan, Z.Y. Yu, S.J. Hu, et al., Angew. Chem. Int. Ed. 58 (2019) 15772–15777.
doi: 10.1002/anie.201909939
F. Lei, Y. Sun, K. Liu, et al., J. Am. Chem. Soc. 136 (2014) 6826–6829.
doi: 10.1021/ja501866r
Y. Li, M. Wen, Y. Wang, et al., Angew. Chem. Int. Ed. 60 (2021) 910–916.
doi: 10.1002/anie.202010156
T. Ling, D.Y. Yan, H. Wang, et al., Nat. Commun. 8 (2017) 1509.
doi: 10.1038/s41467-017-01872-y
J. Deng, H. Li, S. Wang, et al., Nat. Commun. 8 (2017) 14430.
doi: 10.1038/ncomms14430
X. Ren, C. Wei, Y. Sun, et al., Adv. Mater. 32 (2020) 2001292.
doi: 10.1002/adma.202001292
L. Zhang, W. Cai, N. Bao, et al., Adv. Mater. 33 (2021) 2100745.
doi: 10.1002/adma.202100745
Y. Shi, J. Wang, C. Wang, et al., J. Am. Chem. Soc. 137 (2015) 7365–7370.
doi: 10.1021/jacs.5b01732
Y. Guo, Y. Tong, P. Chen, et al., Adv. Mater. 27 (2015) 5989–5994.
doi: 10.1002/adma.201502024
Z.W. Seh, J. Kibsgaard, C.F. Dickens, et al., Science 355 (2017) eaad4998.
doi: 10.1126/science.aad4998
I. Roger, M.A. Shipman, M.D. Symes, et al., Nat. Rev. Chem. 1 (2017) 0003.
doi: 10.1038/s41570-016-0003
H. Sun, L. Chen, Y. Lian, et al., Adv. Mater. 32 (2020) 2006784.
doi: 10.1002/adma.202006784
J. Cao, C. Lei, J. Yang, et al., J. Mater. Chem. A 6 (2018) 18877.
doi: 10.1039/C8TA08337A
K. Wang, Wang X, Li Z, et al., Nano Energy 77 (2020) 105162.
doi: 10.1016/j.nanoen.2020.105162
L. An, J. Feng, Y. Zhang, et al., Adv. Funct. Mater. 29 (2019) 1805298.
doi: 10.1002/adfm.201805298
L. Wang, Z. Li, K. Wang, et al., Nano Energy 74 (2020) 104850.
doi: 10.1016/j.nanoen.2020.104850
C. Lei, S. Lyu, J. Si, et al., ChemCatChem 11 (2019) 5855–5874.
doi: 10.1002/cctc.201901707
F. Cheng, L. Wang, H. Wang, et al., Nano Energy 71 (2020) 104621.
doi: 10.1016/j.nanoen.2020.104621
C. Liu, J. Qian, Y. Ye, et al., Nat. Catal. 4 (2021) 36–45.
doi: 10.1038/s41929-020-00550-5
S.L. Zhang, B.Y. Guan, X.F. Lu, et al., Adv. Mater. 32 (2020) 2002235.
doi: 10.1002/adma.202002235
T. Wu, S. Sheng, J. Song, et al., Nat Catal. 2 (2019) 763–772.
doi: 10.1038/s41929-019-0325-4
J. Kim, H. Jung, S.M. Jung, et al., J. Am. Chem. Soc. 143 (2021) 1399–1408.
doi: 10.1021/jacs.0c10661
Q. Zhao, Z. Yan, C. Chen, et al., Chem. Rev. 117 (2017) 10121–10211.
doi: 10.1021/acs.chemrev.7b00051
J. Li, D. Chu, H. Dong, et al., J. Am. Chem. Soc. 142 (2020) 50–54.
doi: 10.1021/jacs.9b10882
J. Bao, X. Zhang, B. Fan, et al., Angew. Chem. Int. Ed. 54 (2015) 7399–7404.
doi: 10.1002/anie.201502226
Y. Sun, H. Liao, J. Wang, et al., Nat Catal. 3 (2020) 554–563.
doi: 10.1038/s41929-020-0465-6
Y. Duan, J.Y. Lee, S. Xi, et al., Angew. Chem., Int. Ed. 60 (2021) 7418–7425.
doi: 10.1002/anie.202015060
Y. Wen, P. Chen, L. Wang, et al., J. Am. Chem. Soc. 143 (2021) 6482–6490.
doi: 10.1021/jacs.1c00384
J. Yin, J. Jin, M. Lu, et al., J. Am. Chem. Soc. 142 (2020) 18378–18386.
doi: 10.1021/jacs.0c05050
R. Yang, L. An, Y. Zhang, et al., ChemCatChem 11 (2019) 6002–6007.
doi: 10.1002/cctc.201901634
J. Yang, B. Chen, X. Liu, et al., Angew. Chem. Int. Ed. 57 (2018) 9495–9500.
doi: 10.1002/anie.201804854
X. Wang, Y. Zheng, W. Sheng, et al., Mater. Today 36 (2020) 125–138.
doi: 10.1016/j.mattod.2019.12.003
X. Liu, F. Liu, J. Yu, et al., Adv. Sci. 7 (2020) 2001526.
doi: 10.1002/advs.202001526
S.Y. Bae, J. Mahmood, I.Y. Jeon, et al., Nanoscale Horiz. 5 (2020) 43–56.
doi: 10.1039/C9NH00485H
J. Su, Y. Yang, G. Xia, et al., Nat. Commun. 8 (2017) 14969.
doi: 10.1038/ncomms14969
C. Dong, X. Zhang, J. Xu, et al., Small 16 (2020) 1905328.
doi: 10.1002/smll.201905328
C. Wang, L. Qin, Angew. Chem. Int. Ed. 59 (2020) 17219–17224.
doi: 10.1002/anie.202005436
S. Jiang, R. Zhang, H. Liu, et al., J. Am. Chem. Soc. 142 (2020) 6461–6466.
doi: 10.1021/jacs.9b13915
Q. Lu, Y. Yu, Q. Ma, et al., Adv. Mater. 28 (2016) 1917–1933.
doi: 10.1002/adma.201503270
S.H. Ye, Z.X. Shi, J.X. Feng, et al., Angew. Chem. Int. Ed. 57 (2018) 2672–2676.
doi: 10.1002/anie.201712549
J. Yin, J. Jin, H. Zhang, et al., Angew. Chem. Int. Ed. 58 (2019) 18676–18682.
doi: 10.1002/anie.201911470
Y. Gu, A. Wu, Y. Jiao, et al., Angew. Chem. Int. Ed. 60 (2021) 6673–6681.
doi: 10.1002/anie.202016102
J. Yin, J. Jin, H. Liu, et al., Adv. Mater. 32 (2020) 2001651.
doi: 10.1002/adma.202001651
T.X. Nguyen, Y.C. Liao, C.C. Lin, et al., Adv. Funct. Mater. 31 (2021) 2101632.
doi: 10.1002/adfm.202101632
T. Zhao, X. Shen, Y. Wang, et al., Adv. Funct. Mater. 31 (2021) 2100614.
doi: 10.1002/adfm.202100614
J. Gao, C.Q. Xu, S.F. Hung, et al., J. Am. Chem. Soc. 141 (2019) 3014–3023.
doi: 10.1021/jacs.8b11456
D.J. Morgan, Surface Interf. Anal. 47 (2015) 1072–1079.
doi: 10.1002/sia.5852
J. Yang, C. Wang, H. Ju, et al., Adv. Funct. Mater. 27 (2017) 1703864.
doi: 10.1002/adfm.201703864
Y. Duan, Z.Y. Yu, S.J. Hu, et al., Angew. Chem. Int. Ed. 58 (2019) 15772–15777.
doi: 10.1002/anie.201909939
F. Lei, Y. Sun, K. Liu, et al., J. Am. Chem. Soc. 136 (2014) 6826–6829.
doi: 10.1021/ja501866r
Y. Li, M. Wen, Y. Wang, et al., Angew. Chem. Int. Ed. 60 (2021) 910–916.
doi: 10.1002/anie.202010156
T. Ling, D.Y. Yan, H. Wang, et al., Nat. Commun. 8 (2017) 1509.
doi: 10.1038/s41467-017-01872-y
J. Deng, H. Li, S. Wang, et al., Nat. Commun. 8 (2017) 14430.
doi: 10.1038/ncomms14430
X. Ren, C. Wei, Y. Sun, et al., Adv. Mater. 32 (2020) 2001292.
doi: 10.1002/adma.202001292
L. Zhang, W. Cai, N. Bao, et al., Adv. Mater. 33 (2021) 2100745.
doi: 10.1002/adma.202100745
Y. Shi, J. Wang, C. Wang, et al., J. Am. Chem. Soc. 137 (2015) 7365–7370.
doi: 10.1021/jacs.5b01732
Y. Guo, Y. Tong, P. Chen, et al., Adv. Mater. 27 (2015) 5989–5994.
doi: 10.1002/adma.201502024
Liwei Hou , Xianyun Peng , Siliu Lyu , Zhongjian Li , Bin Yang , Qinghua Zhang , Qinggang He , Lecheng Lei , Yang Hou . Advancements in MXene-based nanohybrids for electrochemical water splitting. Chinese Chemical Letters, 2025, 36(6): 110392-. doi: 10.1016/j.cclet.2024.110392
Tianli Hui , Tao Zheng , Xiaoluo Cheng , Tonghui Li , Rui Zhang , Xianghai Meng , Haiyan Liu , Zhichang Liu , Chunming Xu . A review of plasma treatment on nano-microstructure of electrochemical water splitting catalysts. Chinese Journal of Structural Chemistry, 2025, 44(3): 100520-100520. doi: 10.1016/j.cjsc.2025.100520
Chunru Liu , Ligang Feng . Advances in anode catalysts of methanol-assisted water-splitting reactions for hydrogen generation. Chinese Journal of Structural Chemistry, 2023, 42(10): 100136-100136. doi: 10.1016/j.cjsc.2023.100136
Kai Han , Guohui Dong , Ishaaq Saeed , Tingting Dong , Chenyang Xiao . Boosting bulk charge transport of CuWO4 photoanodes via Cs doping for solar water oxidation. Chinese Journal of Structural Chemistry, 2024, 43(2): 100207-100207. doi: 10.1016/j.cjsc.2023.100207
Jijoe Samuel Prabagar , Kumbam Lingeshwar Reddy , Dong-Kwon Lim . Visible-light responsive gold nanoparticle and nano-sized Bi2O3-x sheet heterozygote structure for efficient photocatalytic conversion of N2 to NH3. Chinese Journal of Structural Chemistry, 2025, 44(4): 100564-100564. doi: 10.1016/j.cjsc.2025.100564
Hongye Bai , Lihao Yu , Jinfu Xu , Xuliang Pang , Yajie Bai , Jianguo Cui , Weiqiang Fan . Controllable Decoration of Ni-MOF on TiO2: Understanding the Role of Coordination State on Photoelectrochemical Performance. Chinese Journal of Structural Chemistry, 2023, 42(10): 100096-100096. doi: 10.1016/j.cjsc.2023.100096
Shenghui Tu , Anru Liu , Hongxiang Zhang , Lu Sun , Minghui Luo , Shan Huang , Ting Huang , Honggen Peng . Oxygen vacancy regulating transition mode of MIL-125 to facilitate singlet oxygen generation for photocatalytic degradation of antibiotics. Chinese Chemical Letters, 2024, 35(12): 109761-. doi: 10.1016/j.cclet.2024.109761
Jinshu Huang , Zhuochun Huang , Tengyu Liu , Yu Wen , Jili Yuan , Song Yang , Hu Li . Modulating single-atom Co and oxygen vacancy coupled motif for selective photodegradation of glyphosate wastewater to circumvent toxicant residue. Chinese Chemical Letters, 2025, 36(5): 110179-. doi: 10.1016/j.cclet.2024.110179
Wenhao Chen , Jian Du , Hanbin Zhang , Hancheng Wang , Kaicheng Xu , Zhujun Gao , Jiaming Tong , Jin Wang , Junjun Xue , Ting Zhi , Longlu Wang . Surface treatment of GaN nanowires for enhanced photoelectrochemical water-splitting. Chinese Chemical Letters, 2024, 35(9): 109168-. doi: 10.1016/j.cclet.2023.109168
Lina Wang , Hairu Wang , Qian Bu , Qiong Mei , Junbo Zhong , Bo Bai , Qizhao Wang . Al-O bridged NiFeOx/BiVO4 photoanode for exceptional photoelectrochemical water splitting. Chinese Chemical Letters, 2025, 36(4): 110139-. doi: 10.1016/j.cclet.2024.110139
Xinxin Zhang , Zhijian Liang , Xu Zhang , Qian Guo , Ying Xie , Lei Wang , Honggang Fu . Electronic modulation of VN on Co5.47N as tri-functional electrocatalyst for constructing zinc-air battery to drive water splitting. Chinese Chemical Letters, 2025, 36(5): 109935-. doi: 10.1016/j.cclet.2024.109935
Entian Cui , Yulian Lu , Zhaoxia Li , Zhilei Chen , Chengyan Ge , Jizhou Jiang . Interfacial B-O bonding modulated S-scheme B-doped N-deficient C3N4/O-doped-C3N5 for efficient photocatalytic overall water splitting. Chinese Chemical Letters, 2025, 36(1): 110288-. doi: 10.1016/j.cclet.2024.110288
Hualin Jiang , Wenxi Ye , Huitao Zhen , Xubiao Luo , Vyacheslav Fominski , Long Ye , Pinghua Chen . Novel 3D-on-2D g-C3N4/AgI.x.y heterojunction photocatalyst for simultaneous and stoichiometric production of H2 and H2O2 from water splitting under visible light. Chinese Chemical Letters, 2025, 36(2): 109984-. doi: 10.1016/j.cclet.2024.109984
Gang Hu , Chun Wang , Qinqin Wang , Mingyuan Zhu , Lihua Kang . The controlled oxidation states of the H4PMo11VO40 catalyst induced by plasma for the selective oxidation of methacrolein. Chinese Chemical Letters, 2025, 36(2): 110298-. doi: 10.1016/j.cclet.2024.110298
Yunxia Liu , Guandong Wu , Lin Li , Yiming Niu , Bingsen Zhang , Botao Qiao , Junhu Wang . Construction of sintering-resistant gold catalysts via ascorbic-acid inducing strong metal-support interactions. Chinese Chemical Letters, 2025, 36(4): 110608-. doi: 10.1016/j.cclet.2024.110608
Yanyu Jin , Wenzhe Si , Xing Yuan , Hongjun Cheng , Bin Zhou , Li Cai , Yu Wang , Qibao Wang , Junhua Li . Tuning TM–O interaction by acid etching in perovskite catalysts boosting catalytic performance. Chinese Chemical Letters, 2025, 36(5): 110260-. doi: 10.1016/j.cclet.2024.110260
Zuyou Song , Yong Jiang , Qiao Gou , Yini Mao , Yimin Jiang , Wei Shen , Ming Li , Rongxing He . Promoting the generation of active sites through "Co-O-Ru" electron transport bridges for efficient water splitting. Chinese Chemical Letters, 2025, 36(4): 109793-. doi: 10.1016/j.cclet.2024.109793
Shuyuan Pan , Zehui Yang , Fang Luo . Ni-based electrocatalysts for urea assisted water splitting. Chinese Journal of Structural Chemistry, 2024, 43(8): 100373-100373. doi: 10.1016/j.cjsc.2024.100373
Kun Wang , Jiaxuan Qiu , Zefei Wu , Yang Liu , Yongqi Liu , Xiangpeng Chen , Bao Zang , Jianmei Chen , Yunchao Lei , Longlu Wang , Qiang Zhao . Wafer-level GaN-based nanowires photocatalyst for water splitting. Chinese Chemical Letters, 2025, 36(3): 109993-. doi: 10.1016/j.cclet.2024.109993
Ji Chen , Yifan Zhao , Shuwen Zhao , Hua Zhang , Youyu Long , Lingfeng Yang , Min Xi , Zitao Ni , Yao Zhou , Anran Chen . Heterogeneous bimetallic oxides/phosphides nanorod with upshifted d band center for efficient overall water splitting. Chinese Chemical Letters, 2024, 35(9): 109268-. doi: 10.1016/j.cclet.2023.109268