FERROFERRIC OXIDE/CHITOSAN SCAFFOLDS WITH THREE-DIMENSIONAL ORIENTED STRUCTURE

Received Date: 16 June 2011
Revised Date: 22 September 2011

Fund Project: This work was financially supported by the National Natural Science Foundation of China (Nos. 21104067 and 50773070), China Postdoctoral Science Foundation (No. 20100480085), Key Basic Research Development Plan (973) of China (No. 2009CB930104) and Grand Science and Technology Special Project of Zhejiang Province (No. 2008C11087).

A facile approach to construct ferroferric oxide/chitosan composite scaffolds with three-dimensional oriented structure has been explored in this research. Chitosan and ferroferric oxide are co-precipitated by using an in situ precipitation method, and then lyophilized to get the composite scaffolds. XRD indicated that Fe3O4 was generated during the gel formation process, and increasing the content of magnetic particles could destruct the crystal structure of chitosan. When the content of magnetic particles is lower than 10%, the layer-by-layer structure and wheel spoke structure are coexisting in the scaffolds. Increasing the content of magnetic particles, just layer-by-layer structure could be observed in the scaffolds. Ferroferric oxide particles were uniformly distributed in the matrix, the size of which was about 0.48 m in diameter, 2 m in length. Porosity of magnetic chitosan composite scaffolds is about 90%. When the ratio of ferroferric oxide to chitosan is 5/100, the compressive strength of the material is 0.4367 MPa, which is much higher than that of pure chitosan scaffolds, indicating that the layer-by-layer and wheel spokes complex structure is beneficial for the improvement of the mechanical properties of chitosan scaffolds. However, increasing the content of ferroferric oxide, the compressive strength of scaffolds decreased, because of the decreasing of chitosan crystallization and aggregation of magnetic particles as stress centralized body. Another reason is that the layer-by-layer and wheel spokes complex structure makes bigger contributions for the compressive strength than the layer-by-layer structure does. Three-dimensional ferroferric oxide/chitosan scaffolds could be used as hyperthermia generator system, improving the local circulation of blood, promoting the aggradation of calcium salt and stimulating bone tissue regeneration.
- Chitosan
1. [1]
1. [1]
  Lian Jin , Juan Zhang , Libo Nie , Yan Deng , Ghulam Jilany Khana , Nongyue He . Chitosan nanoparticles act as promising carriers of microRNAs to brain cells in neurodegenerative diseases. Chinese Chemical Letters, 2025, 36(10): 110774-. doi: 10.1016/j.cclet.2024.110774
2. [2]
  Sajid Hussain , Omer M.A. Dagah , Essam A.M.S Obaid , Peng Jin , Ovas Ahmed Dar , Muhammd Irfan , Yiming Qi , Qinghua Wu , Ming Jin , Tengli Zhang , Lei Luo . Chitosan as oral absorption enhancer and inhibitor: A comprehensive review. Chinese Chemical Letters, 2026, 37(1): 111273-. doi: 10.1016/j.cclet.2025.111273
3. [3]
  Jinjie Lu , Qikai Liu , Yuting Zhang , Yi Zhou , Yanbo Zhou . Antibacterial performance of cationic quaternary phosphonium-modified chitosan polymer in water. Chinese Chemical Letters, 2024, 35(9): 109406-. doi: 10.1016/j.cclet.2023.109406
4. [4]
  Linshan Peng , Qihang Peng , Tianxiang Jin , Zhirong Liu , Yong Qian . Highly efficient capture of thorium ion by citric acid-modified chitosan gels from aqueous solution. Chinese Chemical Letters, 2024, 35(5): 108891-. doi: 10.1016/j.cclet.2023.108891
5. [5]
  Dong-Bing Cheng , Junxin Duan , Haiyu Gao . Experimental Teaching Design on Chitosan Extraction and Preparation of Antibacterial Gel. University Chemistry, 2024, 39(2): 330-339. doi: 10.3866/PKU.DXHX202308053
6. [6]
  Rui TIAN , Jiamin CHAI , Junyu CHEN , Yuan REN , Xuehua SUN , Haoyu LI , Yuecheng ZHANG . Chitosan/silica-coated copper nanoclusters: Synthesis and application in cefixime detection. Chinese Journal of Inorganic Chemistry, 2025, 41(9): 1903-1915. doi: 10.11862/CJIC.20250026
7. [7]
  Rui Li , Ruijie Lu , Libin Yang , Jianwen Li , Zige Guo , Qiquan Yan , Mengjun Li , Yazhuo Ni , Keying Chen , Yaoyang Li , Bo Xu , Mengzhen Cui , Zhan Li , Zhiying Zhao . Immobilization of chitosan nano-hydroxyapatite alendronate composite microspheres on polyetheretherketone surface to enhance osseointegration by inhibiting osteoclastogenesis and promoting osteogenesis. Chinese Chemical Letters, 2025, 36(4): 110242-. doi: 10.1016/j.cclet.2024.110242
8. [8]
  Qian Chen , Anyang Shen , Taotao Huang , Xinya Han , Jian Zhang , Hui Jiang , Renyong Liu , Yong Pan , Kui Zhang . Ultrasensitive and selective detection of chemical nerve agent simulants based on naphthalimide functionalized chitosan as fluorescent nanofibers. Chinese Chemical Letters, 2025, 36(7): 110331-. doi: 10.1016/j.cclet.2024.110331
9. [9]
  Aijia Zhang , Guiyuan Zhao , Guangli Xiang , Rui Chen , Yu Dong , Qijie Diao , Jialin Wang , Xiaohui Lin , Wenxuan Zeng , Tianze Jiang , Jun Wu , Xia Zhao . Barnacle-inspired chitosan glycerin gel for skin protection and wound healing in harsh environments. Chinese Chemical Letters, 2025, 36(8): 110767-. doi: 10.1016/j.cclet.2024.110767
10. [10]
  Xinzhe ZHANG , Jiarong XU , Mochou GAO , Yage LIU , Yanbao ZHAO , Jingzeng CUI , Xueyan ZOU . Silver chloride/chitosan-based chloramine nanohybrid with excellent antibacterial activity: Design and structure characterization as well as Ag⁺-Cl^- synergistic antibacterial effect. Chinese Journal of Inorganic Chemistry, 2026, 42(2): 428-438. doi: 10.11862/CJIC.20250123
11. [11]
  Xing Cao , Xinyu Tian , Yuanyuan Huang , Liping Zhang , Yanpeng Ni , Yu-Zhong Wang . H₃PO₃-protonated chitosan enabling flame-retardant and antibacterial PVA composite films with high strength and toughness through multiple H-bonds and interlocking interfaces. Chinese Chemical Letters, 2025, 36(11): 111382-. doi: 10.1016/j.cclet.2025.111382

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(1619)
HTML views(26)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return