Large Pore Mesoporous MCM-41 Templated from Cetyltriethylammonium Bromide
摘要:
Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nSurf./nSi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.
English
Large Pore Mesoporous MCM-41 Templated from Cetyltriethylammonium Bromide
Abstract:
Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nSurf./nSi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.
-
Key words:
- Mesoporous molecular sieve MCM-41
- / synthesis
- / new template