Citation:
XU Wen, XIAO Wangdong, XU Xi. A STUDY ON MECHANICAL PROPERTIES OF γ-RAY IRRADIATED HDPE FILLED WITH SERICITE-TRIDYMITE-CRISTOBALITE*[J]. Chinese Journal of Polymer Science,
1998, 16(4): 339-344.
A STUDY ON MECHANICAL PROPERTIES OF γ-RAY IRRADIATED HDPE FILLED WITH SERICITE-TRIDYMITE-CRISTOBALITE*
摘要:
The effect of γ-ray irradiation on the mechanical properties of high densitypolyethylene(HDPE) filled with sericite-tridymite-cristobalite(STC) was studied. The ex-perimental results show that γ-ray irradiation can improve the affinity between HDPE andSTC, and the dispersion of STC in HDPE matrix. Compared with HDPE/STC (80/20)blend, the yield stress and impact strength of irradiated HDPE (10kGy)/STC (80/20) blendare increased from 22.8 MPa and 70J/m to 28.5 MPa and 144J/m. The yield stress andimpact strength of HDPE/irradiated HDPE/STC (48/32/20) are 27.8MPa and 210J/m,respectively.
English
A STUDY ON MECHANICAL PROPERTIES OF γ-RAY IRRADIATED HDPE FILLED WITH SERICITE-TRIDYMITE-CRISTOBALITE*
Abstract:
The effect of γ-ray irradiation on the mechanical properties of high densitypolyethylene(HDPE) filled with sericite-tridymite-cristobalite(STC) was studied. The ex-perimental results show that γ-ray irradiation can improve the affinity between HDPE andSTC, and the dispersion of STC in HDPE matrix. Compared with HDPE/STC (80/20)blend, the yield stress and impact strength of irradiated HDPE (10kGy)/STC (80/20) blendare increased from 22.8 MPa and 70J/m to 28.5 MPa and 144J/m. The yield stress andimpact strength of HDPE/irradiated HDPE/STC (48/32/20) are 27.8MPa and 210J/m,respectively.